Methods of investigation of the processes of corrosion-mechanical destruction and hydrogenation of metals (review)

Part 2. Formation of passive films and hydrogen sulfide cracking of steels
Laptev A.B., Zakirova L.I., Zagorskikh O.A., Pavlov M.R., Gorbovets M.A.
UDC
621.833: 621.852
DOI
10.18577/2307-6046-2022-0-5-138-146
Article PDF (Russian) (639.06 KB)
How to cite
Laptev A.B., Zakirova L.I., Zagorskikh O.A., Pavlov M.R., Gorbovets M.A. Methods of investigation of the processes of corrosion-mechanical destruction and hydrogenation of metals (review). Part 2. Formation of passive films and hydrogen sulfide cracking of steels // Proceedings of VIAM. 2022. No. 5. DOI: 10.18577/2307-6046-2022-0-5-138-146. URL: https://test.viam.ru/en/journal/2022/5/12
Keywords
corrosion-mechanical destruction, hydrogen sulfide cracking, metal hydrogenation, hydrogen brittleness, slow stretching, crack development, corrosive environment
Abstract

Considers the main stages of the process of formation of protective passive films on steel in a hydrogen sulfide-containing environment and the destruction of metal materials under the simultaneous influence of a corrosive environment and mechanical loads. The main theories and practical results of determining changes in the mechanical characteristics of steel under the influence of a corrosive environment and mechanical loads are presented. As the main criteria for corrosion destruction of materials taken values relative narrowing, relative elongation, and the strength limit during slow tension.

Reference list
  1. Kablov E.N., Evgenov A.G., Mazalov I.S., Shurtakov S.V., Zaitsev D.V., Prager S.M. Structure and properties of EP648 and VZh159 alloys synthesized by selective laser melting after simulation annealing. Materialovedenie, 2020, no. 6, pp. 3–10.
  2. Kablov E.N. Present and future of additive technologies. Metally Evrazii, 2017, no. 1, pp. 2–6.
  3. Kablov E.N., Erofeev V.T., Dergunova A.V. et al. Influence of environmental factors on the processes of biodegradation of vinylester composites. Journal of Physics: Conference Series, 2020, pр. 012029. DOI: 10.1088/1742-6596/1687/1/012029.
  4. Laptev A.B., Nikolaev E.V., Kurshev E.V., Goryashnik Yu.S. Features of biodegradation of thermoplastics based on polyesters in different climatic zones. Trudy VIAM, 2019, no. 7 (79), paper no. 10. Available at: http://www.viam-works.ru (accessed: November 2, 2021). DOI: 10.18577/2307-6046-2019-0-7-84-91.
  5. Gonik A.A. Hydrogen sulfide corrosion and measures to prevent it. Moscow: Nedra, 1966, 167 p.
  6. Getsov L.B., Laptev A.B., Puzanov A.I. et al. Strength of powder material for GTE disks under the aggressive action of a mixture of sodium chlorides and sulfates. Aviatsionnaya tekhnika, 2019, no. 12, pp. 14–25.
  7. Gutman E.M. Mechanochemistry of metals and corrosion protection. Moscow: Metallurgiya, 1974, 232 p.
  8. Erasov V.S., Oreshko E.I. Reasons for dependence of mechanical characteristics of material fracture resistanceon sample sizes. Aviaсionnye materialy i tehnologii, 2018, no. 3, pp. 56–64. DOI: 10.18577/2071-9140-2018-0-3-56-64.
  9. Burran J., Geretta E., Veini L. et al. Contribute to the interpretation of the Strain Rate Effect on type 304 stainless steel ingranular Stress Corrosion Cracking. Corrosion Science, 1985, no. 8, pp. 805–813.
  10. Ebtehai K., Hardie D., Parkins R.N. The Stress Corrosion and preexposure embrittelement of Titanium in Methanolic Solutions of hydrochlorioal acid. Corrosion Science, 1985, no. 6, pp. 415–429.
  11. Zhang K., Zhang J., Jin W. et al. Characterization of fatigue crack propagation of pitting-corroded rebars using weak magnetic signals. Engineering Fracture Mechanics, 2021, vol. 257, art. 108033.
  12. Kasahara K., Sato T. Environ mental factors that influence the susceptibility of line pipe steels to external stress corrosion cracking. Tetsu to hagane, Iron and steel Inst. 1983, vol. 69, no. 11, pp. 1463–1470.
  13. Fot A.P. Development of a complex of experimental equipment and methods of corrosion-mechanical testing: thesis, Dr. Sc. (Tech.). Kurgan: Kurgan State University, 1998, 460 p.
  14. Nenk F., de Long. Evaluation of the Constant Strain Rate Test Method for Testing Stress Corrosion Cracking in Aluminum Alloys. Corrosion, 1978, vol. 34, no. 1, pp. 32–36.
  15. Roogen D., Bulischeck T.S. Stress corrosion cracking of alloy 600 using the constant strain rate test. Corrosion, 1981, vol. 37, no. 10, pp. 597–607.
  16. Grinevich A.V., Laptev A.B., Skripachev S.Yu., Nuzhnyj G.A. Matrix strength characteristics for the assessment of limit states of structural metallic materials. Aviacionnye materialy i tehnologii, 2018, no. 2 (51), pp. 67–74. DOI: 10.18577/2071-9140-2018-0-2-67-74.
  17. Deegan D.C., Wilde B.E. Stress Corrosion Cracking Behavior of ASTM A517 Grade F Steel in Liquid Ammonia Environments. Corrosion – NACE, 1973, vol. 29, no. 8, pp. 310–315.
  18. Xasahara K., Haruhiko A. Effect of Catodic Protection Conditions on the Stress Corrosion Cracking of Line Pipe Steels. Teysu to hagane, Iron and Steel Institution, 1983, vol. 69, no. 14, pp. 1630–1637.
  19. Andresen P., Duguette D. Slow streln rate Stress Corrosion Testing at Elevated Temperatures and High Pressures. Corrosion Science, 1980, vol. 20, pp. 211–223.
  20. Pan Y., Wang Y., Guo F. et al. Stress corrosion behavior of friction stir welding joint of 7N01 aluminum alloy. Journal of Materials Research and Technology, 2021, vol. 15, pp. 1130–1144.
  21. Turn I.E., Wilde B.E., Troiano C.A. On the Sulfide Stress Cracking of line pipe steels. Corrosion, 1983, vol. 39, no. 9, pp. 364–370.
  22. Rajasekaran R., Lakshminarayanan A.K. Probing the stress corrosion cracking resistance of laser beam welded AISI 316LN austenitic stainless steel. Proceedings of the Institution of Mechanical Engineers. Part C: Journal of Mechanical Engineering Science, 2021, vol. 235 (17), pp. 3299–3317.
  23. Fot A.P. Experimental Equipment and Methods for Corrosion-Mechanical Testing: An Analytical Review of Research Results on Objects Exposed to Hydrogen Sulfide-Containing Environments. Orenburg: OGU, 1997, 77 p.
  24. Physical metallurgy. Ed. R.U. Kahn, P. Haazen. 3rd ed., revised. and ad. Moscow: Metallurgiya, 1987, vol. 1: Atomic structure of metals and alloys, 640 p.
  25. Erasov V.S., Oreshko E.I., Lutsenko A.N. Formation of new surfaces in a firm body at stages of elastic and plastic deformations, the beginning and destruction development. Trudy VIAM, 2018, no. 2, paper no. 12. Available at: http://www.viam-works.ru (accessed: July 4, 2021). DOI: 10.18577/2307-6046-2018-0-2-12-12.
  26. Fot A.P., Mullabaev A.A., Kushnarenko V.M., Reshetov S.Yu. Force analysis of multi-position loaders. Zavodskaya laboratoriya. Diagnostika materialov, 1993, no. 6, pp. 55–57.
  27. Laurent P.J. Approximation and optimization. Moscow: Mir, 1975, 357 p.
  28. API Specification 51X for High-Test Line Pipe. Dallas, 1987, p. 9.
  29. Levina Z.M., Reshetov D.N. Contact stiffness of machines. Moscow: Mashinostroenie, 1971, 264 p.