Crystalline corrosion deformable aluminum alloys during natural and natural accelerated corrosion tests

Abramova M.G., Goncharov A.A.
UDC
620.193:669.715
DOI
10.18577/2307-6046-2019-0-11-85-94
Article PDF (Russian) (785.6 KB)
How to cite
Abramova M.G., Goncharov A.A. Crystalline corrosion deformable aluminum alloys during natural and natural accelerated corrosion tests // Proceedings of VIAM. 2019. No. 11. DOI: 10.18577/2307-6046-2019-0-11-85-94. URL: https://test.viam.ru/en/journal/2019/11/10
Keywords
intergranular corrosion, aluminum alloys, field corrosion tests, field accelerated tests.
Abstract

The basic laws of the development of intergranular corrosion of aluminum alloys after full-scale and full-scale accelerated tests in a moderately warm climate of the coastal zone depending on the alloying system are considered. The effect of the geometric grain sizes of alloys of various systems on the depth of the MCC is shown. The dependences of the loss of mechanical properties under tension on the depth of the MCC for sheets of aluminum alloys with a thickness of 2 mm are established. The data obtained can be used to predict changes in mechanical properties under tension, depending on the degree of development of intergranular corrosion.

Reference list
  1. Kablov E.N. Innovacionnye razrabotki FGUP «VIAM» GNC RF po realizacii «Strategicheskih napravlenij razvitiya materialov i tehnologij ih pererabotki na period do 2030 goda» [Innovative developments of FSUE «VIAM» SSC of RF on realization of «Strategic directions of the development of materials and technologies of their processing for the period until 2030»] // Aviacionnye materialy i tehnologii. 2015. №1 (34). S. 3–33. DOI: 10.18577/2071-9140-2015-0-1-3-33.
  2. Antipov V.V. Strategiya razvitiya titanovyh, magnievyh, berillievyh i alyuminievyh splavov [Strategy of development of titanium, magnesium, beryllium and aluminum alloys] // Aviacionnye materialy i tehnologii. 2012. №S. S. 157–167.
  3. Kablov E.N., Startsev O.V., Medvedev I.M. Obzor zarubezhnogo opyta issledovanij korrozii i sredstv zashhity ot korrozii [Review of international experience on corrosion and corrosion protection] // Aviacionnye materialy i tehnologii. 2015. №2 (35). S. 76–87. DOI: 10.18577/2071-9140-2015-0-2-76-87.
  4. Kablov E.N., Startsev O.V., Medvedev I.M. Korrozionnaya agressivnost primorskoy atmosfery. Ch. 2. Novye podkhody k otsenke korrozivnosti primorskikh atmosfer [Corrosive aggressiveness of the coastal atmosphere. Part 2. New approaches to assessing the corrosivity of coastal atmospheres] // Korroziya: materialy, zashchita, 2016. №1. S. 1–15.
  5. Zubarev A.P., Lapayev A.V., Lapayev V.P. Ispolzovaniye obobshchennogo parametra korrozionnogo porazheniya dlya otsenki dolgovechnosti elementov konstruktsiy s korrozionnymi porazheniyami [The use of a generalized parameter of corrosion damage to assess the durability of structural elements with corrosion damage] // Nauchnyy vestnik Mos. gos. tekhn. un-ta grazhdanskoy aviatsii. 2007. №119. S. 30–32.
  6. Akopyan K.E., Lapaev A.V., Semin A.V. Analiz korrozionnogo sostoyaniya samoletov Tu-154m OAO Aviakompanii «AEROFLOT-RAL» po dannym materialov tekhnicheskogo obsluzhivaniya v obeme formy «2» [Analysis of the corrosion state of Tu-154m aircraft of AEROFLOT-RAL Airlines according to the data of maintenance materials in the form of «2»] // Nauchnyy vestnik Mos. gos. tekhn. un-ta grazhdanskoy aviatsii. 2007. №119. S. 24–29.
  7. Kurs M.G., Antipov V.V., Lutsenko A.N., Kutyrev A.E. Integralnyj koeffitsient korrozionnogo razrusheniya deformiruemykh alyuminievykh splavov [Integral figure of corrosion damage of deformed aluminum alloys] // Aviacionnye materialy i tehnologii. 2016. №3 (42). S. 24–32. DOI: 10.18577/2071-9140-2016-0-3-24-32.
  8. Kurs M.G. Prognozirovaniye prochnostnykh svoystv obshivki LA iz deformiruyemogo alyuminiyevogo splava V95o.ch.-T2 s primeneniyem integralnogo koeffitsiyenta korrozionnogo razrusheniya [Forecasting the strength properties of the skin cover of a deformable aluminum alloy В95о.ч.-Т2 with the use of the integrated corrosion reduction coefficient] // Trudy VIAM: elektron. nauch.-tehnich. zhurn. 2018. №5. St. 11. Available at: http://www.viam-works.ru (accessed: August 03, 2018). DOI: 10.18577/2307-6046-2018-0-5-101-109.
  9. Zhang X., Zhou X., Hashimoto T. et al. The influence of grain structure on the corrosion behaviour of 2A97-T3 Al–Cu–Li alloy // Corrosion Science. 2016. Vol. 116. P. 14–21. DOI: 10.1016/j.corsci.2016.12.005.
  10. Liu Y., Pan Q., Li H. et al. Revealing the evolution of microstructure, mechanical property and corrosion behavior of 7A46 aluminum alloy with different ageing treatment // Journal of Alloys and Compounds. 2019. Vol. 792. P. 32–45.
  11. De Bonfils-Lahovary M.-L., Laffont L. Characterization of intergranular corrosion defects in a 2024T351 aluminium alloy // Corrosion Science. 2017. No. 119. P. 60–67. DOI: 10.1016/j.corsci.2017.02.020.
  12. Zhang X., Zhou X., Hashimoto T. et al. Localized corrosion in AA2024-T351 aluminium alloy: Transition from intergranular corrosion to crystallographic pitting // Materials Characterization. 2017. No. 130. P. 230–236. DOI: 10.1016/j.matchar.2017.06.022.
  13. Xu Y., Wang X., Yan Z., Li J. Corrosion Properties of Light-weight and High-strength 2195 Al–Li Alloy // Chinese Journal of Aeronautics. 2011. Vol. 24. P. 681–686.
  14. Roberge P.R., Trethewey K.R. The fractal dimension of corroded aluminium surfaces // Journal of Applied Electrochemistry. 1995. Vol. 25. Issue 10. P. 962–966.
  15. Horvath V.K., Herrmann H.J. The fractal dimension of corrosion cracks // Chaos, Solitons & Fractals. 1991. No. 5. P. 395–400.
  16. De Bonfils-Lahovary M.-L., Josse C., Laffont L., Blanc C. Influence of hydrogen on the propagation of intergranular corrosion defects in 2024 aluminium alloy // Corrosion Science. 2019. Vol. 148. P. 198–205.
  17. Antipov V.V., Senatorova O.G., Tkachenko E.A., Vahromov R.O. Alyuminievye deformiruemye splavy [Aluminum deformable alloys] // Aviacionnye materialy i tehnologii. 2012. №S. S. 167–182.
  18. Khokhlatova L.B., Kolobnev N.I., Oglodkov M.S., Mikhaylov E.D. Alyuminiylitiyevyye splavy dlya samoletostroyeniya [Aluminum-lithium alloys for aircraft construction] // Metallurg. 2012. №5. S. 31–35.
  19. Akimov G.V. Teoriya i metody issledovaniya korrozii metallov [Theory and methods for the study of metal corrosion]. M.–L.: Izd-vo AN SSSR, 1945. 414 s.
  20. Osnovnyye zakonomernosti korrozii alyuminiya [The main laws of corrosion of aluminum] // Tsentralny metallicheskiy portal RF. Available at: http://metallicheckiy-potal.ru/articles/zashita_ot_korrozii_ metalla/aluminii/osnovnie_zakonomernosti_korrozii_alyminia/3 (accessed: September 23, 2019).
  21. Sinyavskiy V.S., Valkov V.D., Kalinin V.D. Korroziya i zashchita alyuminiyevykh splavov [Corrosion and protection of aluminum alloys]. M.: Metallurgiya, 1986. S. 37–43.
  22. GOST 9.021–74. Edinaya sistema zashchity ot korrozii i stareniya (YESZKS). Alyuminiy i splavy alyuminiyevyye. Metody uskorennykh ispytaniy na mezhkristallitnuyu korroziyu [State Standard 9.021–74. Unified system of corrosion and ageing protection. Aluminium and aluminium alloys. Accelerated test methods for intercrystalline corrosion]. M.: Standartinform, 1974. 4 s.
  23. Kurs M.G., Kutyrev A.E. Primeneniye integralnogo koeffitsiyenta korrozionnogo razrusheniya dlya prognozirovaniya izmeneniya prochnostnykh svoystv deformiruyemykh alyuminiyevykh splavov [The use of the integral coefficient of corrosion failure to predict changes in the strength properties of deformable aluminum alloys] // Sovremennoye materialovedeniye: traditsii otechestvennykh nauchnykh shkol i innovatsionnyy podkhod: sb. dokl. Vseros. molodezhnoy nauch.-tekhnich. konf. M.: VIAM, 2017. S. 132–142.
  24. Kurs M.G., Goncharov A.A. Issledovaniye korrozionnogo razrusheniya deformiruyemykh alyuminiyevykh splavov pri naturno-uskorennykh ispytaniyakh. Chast 2. Pittingovaya korroziya [Investigation of corrosion failure of wrought aluminum alloys during field accelerated tests. Part 2. Pitting corrosion] // Voprosy materialovedeniya. 2019. №1 (97). S. 175–187.
  25. GOST 9.908–85. Edinaya sistema zashchity ot korrozii i stareniya (ESZKS). Metally i splavy. Metody opredeleniya pokazateley korrozii i korrozionnoy stoykosti [State Standard 9.908–85. Unified system of corrosion and ageing protection. Metals and alloys. Methods for determining indicators of corrosion and corrosion resistance]. M.: Izd-vo standartov, 1985. 34 s.
  26. Kurs M.G., Laptev A.B., Kutyrev A.Ye., Morozova L.V. Issledovaniye korrozionnogo razrusheniya deformiruyemykh alyuminiyevykh splavov pri naturno-uskorennykh ispytaniyakh. Chast 1 [Investigation of corrosion failure of wrought aluminum alloys during field accelerated tests. Part 1] // Voprosy materialovedeniya. 2016. №1 (85). S. 116–126.