Technological features of the manufacture of thick-walled parts of the PCM (review)

Timoshkov P.N., Khrulkov A.V., Usacheva M.N., Purvin K.E.
UDC
678.8
DOI
10.18577/2307-6046-2019-0-3-61-67
Article PDF (Russian) (543.83 KB)
How to cite
Timoshkov P.N., Khrulkov A.V., Usacheva M.N., Purvin K.E. Technological features of the manufacture of thick-walled parts of the PCM (review) // Proceedings of VIAM. 2019. No. 3. DOI: 10.18577/2307-6046-2019-0-3-61-67. URL: https://test.viam.ru/en/journal/2019/3/7
Keywords
polymer composite materials, thick-walled parts, exothermic effect, vacuum-autoclave molding, technological features, mathematical modeling.
Abstract

Thick-walled parts made of polymer composite materials (PCM) are used in the aviation, railway, construction and other industries. Their manufacture has a special feature – when forming a structure, zones with elevated temperature may appear due to a sharp jump in the exothermic effect, which can lead to residual stresses leading to cracks and delamination, destruction of the material, and even ignition of the part. This review discusses various ways to reduce this effect when forming a structure.

Reference list
  1. StekloTekhnologiya [Elektronnyy resurs]. Available at: http://www.steklo-tech.ru (accessed: January 16, 2019).
  2. Kablov E.N. Innovacionnye razrabotki FGUP «VIAM» GNC RF po realizacii «Strategicheskih napravlenij razvitiya materialov i tehnologij ih pererabotki na period do 2030 goda» [Innovative developments of FSUE «VIAM» SSC of RF on realization of «Strategic directions of the development of materials and technologies of their processing for the period until 2030»] // Aviacionnye materialy i tehnologii. 2015. №1 (34). S. 3–33. DOI: 10.18577/2071-9140-2015-0-1-3-33.
  3. Kablov E.N. Aviatsionnoye materialovedeniye v XXI veke. Perspektivy i zadachi [Aviation Materials in the XXI century. Perspectives and tasks] // Aviaсionnyye materialy. Izbrannyye trudy «VIAM» 1932–2002. M.: MISIS–VIAM, 2002. S. 23–47.
  4. Kablov E.N. Materialy novogo pokoleniya [New generation materials] // Zashchita i bezopasnost. 2014. №4. S. 28–29.
  5. Kablov E.N. Kompozity: segodnya i zavtra [Composites: today and tomorrow] // Metally Evrazii. 2015. №1. S. 36–39.
  6. Mikhaylin Yu.A. Konstruktsionnyye polimernyye kompozitsionnyye materialy [Structural polymer composites]. M.: NOT, 2010. 822 s.
  7. Antyufeeva N.V., Aleksashin V.M., Pavlov M.R., Stolyankov Yu.V. Issledovanie vozmozhnosti ispolzovaniya ugleplastikov v usloviyah arkticheskogo klimata [Research of possibility of use carbon fiber reinforced polymers in the conditions of the Arctic climate] // Aviacionnye materialy i tehnologii. 2016. №4 (45). S. 86–94. DOI: 10.18577/2071-9140-2016-0-4-86-94.
  8. Raskutin A.E. Rossiiskie polimernye kompozitsionnye materialy novogo pokoleniia, ikh osvoenie i vnedrenie v perspektivnykh razrabatyvaemykh konstruktsiiakh [Russian polymer composite materials of new generation, their exploitation and implementation in advanced developed constructions] // Aviacionnye materialy i tehnologii. 2017. №S. S. 349–367. DOI: 10.18577/2071-9140-2017-0-S-349-367.
  9. Donetskiy K.I., Karavayev R.Yu., Tsybin A.I., Veshkin E.A., Mikhaldykin E.S. Konstruktsionnyy stekloplastik dlya izgotovleniya elementov shpuntovykh ograzhdeniy [Constructional fiberglass plastic for manufacturing of enclosing sheeting elements] // Aviatsionnyye materialy i tekhnologii. 2017. №3 (48). S. 56–64. DOI: 10.18577/2071-9140-2017-0-3-56-64.
  10. Dmitriyev O.S., Kirillov V.N., Kavun N.S., Dmitriyev A.O. Raschet i analiz optimalnykh rezhimov otverzhdeniya izdeliy iz stekloplastikov v zavisimosti ot ikh tolshchiny [Calculation and analysis of the optimal modes of curing products made of fiberglass, depending on their thickness] // Plasticheskiye massy. 2011. №10. S. 21–27.
  11. Lipatov Yu.S. Fiziko-khimicheskiye osnovy napolnitelya polimerov [Physico-chemical bases of polymer filler]. M.: Khimiya, 1991. 260 s.
  12. Shut N.I., Sichkar T.G., Voznyy P.A. Vliyaniye struktury granichnogo sloya na teploperenos i molekulyarnuyu podvizhnost napolnennykh epoksidnykh polimerov [Effect of boundary layer structure on heat transfer and molecular mobility of filled epoxy polymers] // Kompozitsionnyye polimernyye materialy. 1985. №24. S. 18–21.
  13. Dmitriyev A.O. Problemy razrabotki tekhnologii i organizatsii proizvodstva tolstostennykh izdeliy iz polimernykh kompozitov [Problems of technology development and organization of production of thick-walled products from polymer composites] // Razvitiye sovremennoy nauki: teoreticheskiye i prikladnyye aspekty. 2016. №7. S. 8–10.
  14. Dmitriyenko Yu.I., Zakharova Yu.V., Sborshchikov S.V. Modelirovaniye protsessa otverzhdeniya tolstostennykh konstruktsiy iz polimernykh kompozitsionnykh materialov [Modeling the process of curing thick-walled structures made of polymer composite materials] // Innovatsionnaya nauka. 2016. №12–4. S. 31–36.
  15. Spravochnik po kompozitsionnym materialam v 2-kh kn. [Handbook of composite materials in 2 books]. M.: Mashinostroyeniye, 1988. Kn. 2. 448 s.
  16. Sposob izgotovleniya tolstostennykh sloistykh izdeliy iz polimernykh kompozitsionnykh materialov: pat. 2271928 Ros. Federatsiya. №2004124281/12 [A method of manufacturing a thick-walled laminated products from polymer composite materials: pat. 2271928 Rus. Federation. No. 2004124281/12]; zayavl. 09.08.04; opubl. 20.03.06.
  17. Sposob polimerizatsii tolstostennykh stekloplastikovykh izdeliy: pat. 505572 SSSR. №1938854/23-5 [Method of polymerization of thick-walled fiberglass products: pat. 505572 USSR. No. 1938854/23-5]; zayavl. 06.07.73; opubl. 05.03.76.
  18. Apparatus for molding and solidifying a resinous composite structure: pat. US 4828472A USA. No. B29C 33/02; field 16.12.83; publ. 09.05.89.
  19. Sposob izgotovleniya krupnogabaritnykh tolstostennykh polimernykh kompozitsionnykh detaley metodom rtm (resin transfer molding): pat. 2376140 Ros. Federatsiya. №2008114728/12 [A method of manufacturing large-sized thick-walled polymer composite parts using the rtm method (resin transfer molding): pat. 2376140 Rus. Federation. No. 2008114728/12]; zayavl. 02.07.08; opubl. 20.12.09.
  20. Sposob izgotovleniya krupnogabaritnykh tolstostennykh polimernykh kompozitnykh detaley: pat. 2301148 Ros. Federatsiya. №2005130459/12 [A method of manufacturing large-sized thick-walled polymer composite parts: pat. 2301148 Rus. Federation. №2005130459/12]; zayavl. 30.09.05; opubl. 20.06.07.
  21. Sposob formovaniya tolstostennykh obolochechnykh konstruktsiy na osnove polimernykh kompozitsionnykh materialov: pat. 2634446 Ros. Federatsiya. №2015156879 [Method of forming thick-walled shell structures based on polymer composite materials: pat. 2634446 Rus. Federation. No. 2015156879]; zayavl. 30.12.15; opubl. 30.10.17.
  22. Dmitriyev O.S., Khudyakov V.V., Dmitriyev A.O. Tekhnologicheskiye problemy proizvodstva tolstostennykh izdeliy iz konstruktsionnykh stekloplastikov [Technological problems of the production of thick-walled products from structural fiberglass] // Nauchnyy vestnik Voronezhskogo gosudarstvennogo arkhitekturno-stroitel'nogo universiteta. Ser.: Fiziko-khimicheskiye problemy i vysokiye tekhnologii stroitel'nogo materialovedeniya. 2014. №2 (9). S. 32–40.
  23. Barinov D.Ya., Mayorova I.A., Marakhovskiy P.S., Zuyev A.V., Kutsevich K.E., Lukina N.F. Matematicheskoye modelirovaniye temperaturnykh poley pri otverzhdenii tolstostennoy plity stekloplastika [Mathematical modeling of temperature fields during curing of thick-walled fiberglass plates] // Perspektivnyye materialy. 2015. №4. S. 5–14.
  24. Sposob izgotovleniya tolstostennykh sloistykh izdeliy iz polimernykh kompozitsionnykh materialov: pat. 2424115 Ros. Federatsiya. №2009139775/05 [A method of manufacturing a thick-walled laminated products from polymer composite materials: Pat. 2424115 Rus. Federation. No. 2009139775/05]; zayavl. 28.10.09; opubl. 20.07.11.
  25. Sposob izgotovleniya tolstostennykh sloistykh izdeliy iz polimernykh kompozitsionnykh materialov: pat. 2286253 Ros. Federatsiya. №2005112423/12 [A method of manufacturing a thick-walled laminated products from polymer composite materials: Pat. 2286253 Rus. Federation. №2005112423/12]; zayavl. 25.04.05; opubl. 27.10.06.
  26. Sokolov V.V., Gusev S.A., Sidorov O.I., Lunkina G.V. Osobennosti temperaturno-vremennogo rezhima otverzhdeniya tolstostennogo organoplastika [Features of the temperature-time mode of curing thick-walled organoplasty] // V Mezhdunar. konferentsiya-shkola po khimicheskoy tekhnologii: sb. tez. dokl. satellitnoy konferentsii XX Mendeleyevskogo yezda po obshchey i prikladnoy khimii. Volgograd: VGTU, 2016. T. 1. S. 568–570.
  27. Tyukov N.I., Dautov A.I., Zakurdayeva Ye.A. Matematicheskaya model upravleniya protsessom razogreva avtoklava pri proizvodstve izdeliy iz kompozitsionnykh materialov [Mathematical model of control of the heating process of the autoclave in the manufacture of products from composite materials] // Vestnik UGATU. 2008. T. 10. №2 (27). S. 159–163.