Testing of samples from three-layer structures with honeycomb filler

Erasov V.S., Sibayev I.G., Sutubalov A.I.
UDC
620.17
DOI
10.18577/2307-6046-2025-0-10-133-155
Article PDF (Russian) (1.44 MB)
How to cite
Erasov V.S., Sibayev I.G., Sutubalov A.I. Testing of samples from three-layer structures with honeycomb filler // Proceedings of VIAM. 2025. No. 10. DOI: 10.18577/2307-6046-2025-0-10-133-155. URL: https://test.viam.ru/en/journal/2025/10/11
Keywords
hree-layer structures, honeycomb filler, sandwich structures, mechanical characteristics
Abstract

A three-layer structure with a honeycomb core (sandwich structure) is presented as a composite material consisting of two coverings as a reinforcing filler, a honeycomb core (matrix) and an adhesive layer as an interphase layer. A detailed review of the methods for testing of samples from three-layer structures with a honeycomb core is given. The following tests are considered: bending, compression, tension, shear, peeling of the covering on a drum, the ability to absorb the energy of external force action, static and impact loading. The main types of destruction of sandwich structures during these tests are reflected. The characteristics of the material determined during these tests are considered. Recommendations for the design of three-layer structures are given.

Reference list
  1. Panin V.F. Structures with honeycomb core. Moscow: Mashinostroenie, 1982, 152 p.
  2. Panin V.F., Gladkov Yu.A. Structures with core: reference book. Moscow: Mashinostroenie, 1991, 272 p.
  3. Giyasov B.I., Seregin N.G., Seregin D.N. Three-layer panels made of polymer composite materials: textbook. Moscow: ASV Publ. House, 2015, 64 p.
  4. Bitzer T. Honeycomb Technology: materials, design, manufacturing, applications and testing. Springer Science + Business Media Dordrecht, 1997, 233 p.
  5. Kassapoglou C. Design and analysis of composite structures with applications to aerospace structures. Wiley, 2010, 308 p.
  6. Gay D. Composite materials. Design and Application. CRC Press, 2015, 598 p.
  7. Castanie B., Bouvet C., Ginat M. Review of composite sandwich structure in aeronautic applications. Composite. Part C, 2020, vol. 1, p. 100004. DOI: 10.1016/j.jcoms.2020.100004.
  8. Sadig S.E., Bakhy S.H., Jweeg M.J. Crashworthiness behavior of aircraft sandwich structure with honeycomb core under bending load. IOP Conference Series: Materials Science and Engineering, 2020, vol. 923, p. 16.
  9. Abdullin I.N. Design of rational three-layer structures with a rod filler: thesis, Cand. Sc. (Tech.). Kazan, 2017, 130 p.
  10. Falchenko Yu.V., Petrushinets L.V. Modern methods for producing three-layer panels from aluminum alloys (review). Avtomaticheskaya svarka, 2018, no. 6, pp. 38–44.
  11. Dimitrienko Yu.I., Fedonyuk N.N., Gubareva E.A., Sborshchikov S.V., Prozorovsky A.A., Yerasov V.S., Yakovlev N.O. Modeling and development of three-layer composite materials with a honeycomb filler. Vestnik MGTU im. N.E. Baumana. Ser.: Estestvennye nauki, 2014, no. 5, pp. 66–81.
  12. Shershak P.V., Yakovlev N.O., Shokin G.I., Kutsevich K.E., Popkova E.A. Evaluation method and factors influencing the bonding quality between face and honey-comb cores in floor and interior aircraft panels. Aviacionnye materialy i tehnologii, 2020, no. 2 (59), pp. 81–88. DOI: 10.18577/2071-9140-2020-0-2-81-88.
  13. Pavlova S.A. Analysis of the contact interaction of a polymer honeycomb core with load-bearing layers in three-layer structures. Vestnik Samarskogo universiteta. Aerokosmicheskaya tekhnika, tekhnologii i mashinostroenie, 2021, vol. 20, no. 1, pp. 87–96. DOI: 10.18287/2541-7533-2021-20-1-87-96.
  14. Ivanov A.A., Kashin S.M., Semenov V.I. New generation of honeycomb fillers for aerospace engineering. Moscow: Energoatomizdat, 2000, 436 p.
  15. ASTM D7249/D7249M–2020. Standard Test Methods for Facesheet Properties of Sandwich Constructions by Long Beam Flexure. American Society for Testing and Materials, 2020, 10 p.
  16. State Standard R 56680–2015. Polymer composites. Determination of mechanical characteristics during bending of the material of the outer layer of sandwich structures by the method of testing a long beam for bending. Moscow: Standartinform, 2016, 33 p.
  17. ASTM C365/C365M–2022. Standard Test Method for Flatwise Compressive Properties of Sandwich Cores. American Society for Testing and Materials, 2022, 8 p.
  18. State Standard R 56816–2023. Polymer composites. Method for determining mechanical characteristics under compression perpendicular to the plane of the sample of the material of the inner layer of sandwich structures. Moscow: Russian Institute of Standardization, 2023, 33 p.
  19. ASTM C297/C297M–2016. Standard Test Method for Flatwise Tensile Strength of Sandwich Constructions. American Society for Testing and Materials, 2024, 8 p.
  20. State Standard R 56783–2019. Polymer composites. Method for determining the tensile strength perpendicular to the plane of sandwich structures. Moscow: Standartinform, 2019, 18 p.
  21. ASTM C364/C364M–2016. Standard Test Method for Edgewise Compressive Strength of Sandwich Constructions. American Society for Testing and Materials, 2024, 8 p.
  22. State Standard R 6809–2023. Polymer composites. Method for determining the ultimate compressive strength parallel to the plane of sandwich structures. Moscow: Russian Institute of Standardization, 2023, 16 p.
  23. ASTM C393/C393M–2020. Standard Test Method for Core Shear Properties of Sandwich Constructions by Beam Flexure. American Society for Testing and Materials, 2020, 8 p.
  24. State Standard R 56791–2023. Polymer composites. Determination of shear strength characteristics of the inner layer material of sandwich structures by beam bending test. Moscow: Standartinform, 2024, 28 p.
  25. ASTM D1781–1998. Standard Test Method for Climbing Drum Peel for Adhesives. American Society for Testing and Materials, 2021, 4 p.
  26. State Standard R 56792–2015. Polymer composites. Method of testing for delamination with winding on a drum. Moscow: Standartinform, 2019, 14 p.
  27. ASTM D7250/D7250M–2020. Standard Practice for Determining Sandwich Beam Flexure and Shear Stiffness. American Society for Testing and Materials, 2020, 7 p.
  28. State Standard R 56798–2015. Polymer composites. Method for determining mechanical characteristics during bending of sandwich structures. Moscow: Standartinform, 2016, 27 p.
  29. ASTM D7336/D7336M–2022. Standard Test Method for Static Energy Absorption Properties of Honeycomb Sandwich Core Materials. American Society for Testing and Materials, 2022, 9 p.
  30. State Standard R 56772–2015. Polymer composites. Method for determining the absorption characteristics of the cellular material of the inner layer of sandwich structures under the influence of static energy. Moscow: Standartinform, 2016, 23 p.
  31. ASTM D7766/D7766M–2016. Standard Practice for Damage Resistance of Sandwich Constructions. American Society for Testing and Materials, 2023, 9 p.
  32. State Standard R 56684–2015. Polymer composites. Method for determining the resistance to destruction of sandwich structures. Moscow: Standartinform, 2016, 22 p.
  33. ASTM C480/C480M–2008. Standard Test Method for Flexure Creep of Sandwich Constructions. American Society for Testing and Materials, 2015, 5 p.
  34. State Standard R 56784–2015. Polymer composites. Method for determining creep in bending of sandwich structures. Moscow: Standartinform, 2016, 15 p.
  35. Volkov A.N. Modeling and calculation of three-layered designs with discrete filler: Cand. Sc. (Tech.). Moscow, 2023, 132 р.
  36. Vishtalov R.I., Muselemov H.M., Ustakhanov O.M. Determination of the reduced characteristics of honeycomb cores of various shapes. Vestnik Dagestanskogo gosudarstvennogo tekhnicheskogo universiteta. Tekhnicheskiye nauki, 2016, no. 42 (3), pp. 155–166. DOI: 10.21822/2073-6185-2016-42-3-155-166.
  37. Petrova A.P., Malysheva G.V. Adhesives, adhesive binders and adhesive prepregs: textbook. Ed. E.N. Kablov. Moscow: VIAM, 2017, pp. 327–330.
  38. ASTM D6264/6264M–2023. Standard Test Method for Measuring the Damage Resistance of Fiber-Reinforced Polymer Matrix Composite to a Concentrated Quasi-Static Indentation Force. American Society for Testing and Materials, 2023, 11 p.
  39. State Standard R 56794–2015. Polymer composites. Method for determining resistance to destruction under concentrated quasi-static indentation load. Moscow: Standartinform, 2016, 23 p.
  40. ASTM D7136/7136M–2020. Standard Test Method for Measuring the Damage Resistance of Fiber-Reinforced Polymer Matrix Composite to a Drop-Weight Impact Event. American Society for Testing and Materials, 2023, 16 p.
  41. State Standard 33496–2015. Polymer composites. Test method for resistance to damage when struck by a falling weight. Moscow: Standartinform, 2016, 18 p.
  42. ASTM C394/C394M–2016. Standard Test Method for Shear Fatique of Sandwich Core Materials. American Society for Testing and Materials, 2024, 6 p.
  43. State Standard R 57049–2016. Polymer composites. Method for determining shear fatigue of materials of the inner layer of sandwich structures. Moscow: Standartinform, 2016, 19 p.
  44. Composite Materials Handbook. SAE International, 2013, Vol.: 6. Structural Sandwich Composites, 352 p.
  45. Burman M. Fatigue Crack Initiation and Propagation in Sandwich Structures. Stockholm: Royal Institute of Technology, 1998, 171 p.
  46. Rumyantsev A.F. Design of cfrp shutter of the effective load compartment for «Buran» reusable spaceship. Aviacionnye materialy i tehnologii, 2013, no. S1, pp. 56–61.
  47. Timoshkov P.N., Kolobkov A.S., Kurnosov A.O., Goncharov V.A. Prepregs based on melt binders and new-generation polymer composite materials based on them for aviation products. Proc. V All-Rus. Sci. and Tech. Conf. «Polymer composite materials and production technologies of the new generation». Moscow: NRC «Kurchatov Institute» – VIAM, 2021, pp. 7–20.
  48. Bolshakov V.A., Antyufeeva N.V. Evaluation of the curing process model of the adhesive binder in prepreg. Aviation materials and technologies, 2023, no. 4 (73), paper no. 07. Available at: http://www.journal.viam.ru (accessed: January 15, 2025). DOI: 10.18577/2713-0193-2023-0-4-66-77.
  49. Samoryadov A.V., Kalugina E.V., Bitt V.V., Parshikov Yu.G., Ergashev A.T. Development and research of the properties of composite materials based on thermo-plastic hybrid polymer matrix. Aviation materials and technologies, 2024, no. 3 (76), paper no. 05. Available at: http://www.journal.viam.ru (accessed: January 15, 2025). DOI: 10.18577/2713-0193-2024-0-3-51-68.
  50. Sutubalov A.I., Podzhivotov N.Yu., Shershak P.V., Yakovlev N.O. Evaluation of homogeneity of physical and mechanical properties of semi-finished products for aviation purpose. Aviation materials and technologies, 2024, no. 1 (74), paper no. 10. Available at: http://www.journal.viam.ru (accessed: January 15, 2025). DOI: 10.18577/2713-0193-2024-0-1-121-135.